{"count":97,"next":"http://glycodata.org/api/gdd/polymer-solubility/?format=json&page=2","previous":null,"results":[{"id":1,"polymer":"Cellulose acetate","solvent":"1,4-dioxane","concentration_mg_ml":"15.01","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"56","transmission_25C":"100","transmission_60C":"100","cloud_point_C":"16","method":"Experiment","conditions":"15.01 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 15.01 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99.8 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=48); observed range 23-100 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in 1,4-dioxane at 15.01 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Approx. cloud point on cooling ~16 °C. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":2,"polymer":"Cellulose acetate","solvent":"1-Octanol","concentration_mg_ml":"14.98","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"48","transmission_25C":"43","transmission_60C":"8","cloud_point_C":"","method":"Experiment","conditions":"14.98 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 14.98 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=186); observed range 8-58 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in 1-Octanol at 14.98 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":3,"polymer":"Cellulose acetate","solvent":"2,4,6-trimethylpyridine","concentration_mg_ml":"15.04","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"76","transmission_25C":"80","transmission_60C":"58","cloud_point_C":"","method":"Experiment","conditions":"15.04 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 15.04 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=209); observed range 38-95 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in 2,4,6-trimethylpyridine at 15.04 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":4,"polymer":"Cellulose acetate","solvent":"Acetonitrile","concentration_mg_ml":"14.96","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Soluble","transmission_10C":"100","transmission_25C":"100","transmission_60C":"100","cloud_point_C":"","method":"Experiment","conditions":"14.96 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 14.96 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99.5 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=51); observed range 100-100 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Acetonitrile at 14.96 mg/mL is soluble: clear (T > 85 %) over the whole 10-60 °C cooling ramp. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":5,"polymer":"Cellulose acetate","solvent":"Anisole","concentration_mg_ml":"14.94","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"100","transmission_25C":"100","transmission_60C":"100","cloud_point_C":"","method":"Experiment","conditions":"14.94 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 14.94 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=52); observed range 83-100 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Anisole at 14.94 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":6,"polymer":"Cellulose acetate","solvent":"Benzene","concentration_mg_ml":"14.91","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"59","transmission_25C":"69","transmission_60C":"78","cloud_point_C":"","method":"Experiment","conditions":"14.91 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 14.91 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=146); observed range 58-100 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Benzene at 14.91 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":7,"polymer":"Cellulose acetate","solvent":"Benzyl alcohol","concentration_mg_ml":"15.04","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"94","transmission_25C":"64","transmission_60C":"100","cloud_point_C":"37","method":"Experiment","conditions":"15.04 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 15.04 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=72); observed range 52-100 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Benzyl alcohol at 15.04 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Approx. cloud point on cooling ~37 °C. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":8,"polymer":"Cellulose acetate","solvent":"Chlorobenzene","concentration_mg_ml":"14.97","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"17","transmission_25C":"25","transmission_60C":"65","cloud_point_C":"","method":"Experiment","conditions":"14.97 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 14.97 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=211); observed range 16-65 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Chlorobenzene at 14.97 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":9,"polymer":"Cellulose acetate","solvent":"Cyclohexanone","concentration_mg_ml":"14.4","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"","transmission_25C":"","transmission_60C":"","cloud_point_C":"","method":"Experiment","conditions":"14.4 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 14.4 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99.8 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=2); observed range 74-74 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Cyclohexanone at 14.4 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":10,"polymer":"Cellulose acetate","solvent":"Cyclopentanone","concentration_mg_ml":"15.02","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Soluble","transmission_10C":"100","transmission_25C":"100","transmission_60C":"100","cloud_point_C":"","method":"Experiment","conditions":"15.02 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 15.02 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=51); observed range 100-100 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Cyclopentanone at 15.02 mg/mL is soluble: clear (T > 85 %) over the whole 10-60 °C cooling ramp. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":11,"polymer":"Cellulose acetate","solvent":"DMF","concentration_mg_ml":"15.14","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Soluble","transmission_10C":"100","transmission_25C":"100","transmission_60C":"100","cloud_point_C":"","method":"Experiment","conditions":"15.14 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 15.14 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99.8 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=51); observed range 100-100 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in DMF at 15.14 mg/mL is soluble: clear (T > 85 %) over the whole 10-60 °C cooling ramp. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":12,"polymer":"Cellulose acetate","solvent":"DMSO","concentration_mg_ml":"14.92","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"0","transmission_25C":"99","transmission_60C":"100","cloud_point_C":"19","method":"Experiment","conditions":"14.92 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 14.92 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99.9 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=46); observed range 0-100 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in DMSO at 14.92 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Approx. cloud point on cooling ~19 °C. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":13,"polymer":"Cellulose acetate","solvent":"Diethyl ether","concentration_mg_ml":"14.92","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Insoluble","transmission_10C":"1","transmission_25C":"1","transmission_60C":"3","cloud_point_C":"","method":"Experiment","conditions":"14.92 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 14.92 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99.8 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=51); observed range 1-3 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Diethyl ether at 14.92 mg/mL is insoluble: turbid (T < 10 %) over the whole 10-60 °C cooling ramp. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":14,"polymer":"Cellulose acetate","solvent":"Ethanol","concentration_mg_ml":"14.92","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"1","transmission_25C":"1","transmission_60C":"1","cloud_point_C":"","method":"Experiment","conditions":"14.92 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 14.92 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 90 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=52); observed range 1-30 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Ethanol at 14.92 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":15,"polymer":"Cellulose acetate","solvent":"Ethyl lactate","concentration_mg_ml":"15.06","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"100","transmission_25C":"100","transmission_60C":"100","cloud_point_C":"26","method":"Experiment","conditions":"15.06 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 15.06 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 98 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=61); observed range 35-100 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Ethyl lactate at 15.06 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Approx. cloud point on cooling ~26 °C. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":16,"polymer":"Cellulose acetate","solvent":"Heptane","concentration_mg_ml":"15","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"99","transmission_25C":"94","transmission_60C":"66","cloud_point_C":"","method":"Experiment","conditions":"15 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 15 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=140); observed range 62-100 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Heptane at 15 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":17,"polymer":"Cellulose acetate","solvent":"Isobutyl acetate","concentration_mg_ml":"14.98","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Insoluble","transmission_10C":"6","transmission_25C":"6","transmission_60C":"6","cloud_point_C":"","method":"Experiment","conditions":"14.98 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 14.98 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=51); observed range 6-6 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Isobutyl acetate at 14.98 mg/mL is insoluble: turbid (T < 10 %) over the whole 10-60 °C cooling ramp. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":18,"polymer":"Cellulose acetate","solvent":"Petroleum ether","concentration_mg_ml":"15.03","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"49","transmission_25C":"42","transmission_60C":"41","cloud_point_C":"","method":"Experiment","conditions":"15.03 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 15.03 mg/mL polymer, Mn 50000 g/mol (Sigma). Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=210); observed range 35-54 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Petroleum ether at 15.03 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":19,"polymer":"Cellulose acetate","solvent":"Pyridine","concentration_mg_ml":"15.36","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"100","transmission_25C":"100","transmission_60C":"100","cloud_point_C":"","method":"Experiment","conditions":"15.36 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 15.36 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=52); observed range 81-100 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Pyridine at 15.36 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."},{"id":20,"polymer":"Cellulose acetate","solvent":"Toluene","concentration_mg_ml":"14.9","molecular_weight":"50000","supplier":"Sigma","solubility_class":"Partially soluble","transmission_10C":"80","transmission_25C":"70","transmission_60C":"73","cloud_point_C":"","method":"Experiment","conditions":"14.9 mg/mL, 10-60 °C, 0.5 °C/min","conditions_detail":"Crystal16 turbidity (645 nm), cooling ramp 60 to 10 °C at 0.5 °C/min after two heat/cool cycles; holds 120 min at 10 °C and 60 min at 60 and 25 °C; stirring 900 rpm. Sample: 14.9 mg/mL polymer, Mn 50000 g/mol (Sigma); solvent purity 99.9 %. Transmission binned per 1 °C (median of Savitzky-Golay filtered cooling-phase points, n=150); observed range 58-100 %. Class thresholds from the source paper: insoluble <10 %, soluble >85 %, partial 10-85 %. Nonequilibrium (0.5 °C/min).","doi":"10.1021/acs.jpcb.4c06500","comments":"Cellulose acetate in Toluene at 14.9 mg/mL is partially soluble: transmission between 10 and 85 % at some temperature on cooling. Class refers to nonequilibrium behaviour during the cooling ramp, not thermodynamic solubility. Data: Amrihesari et al., J. Phys. Chem. B 2024 (github.com/mona2442/Polymer-Solubility-Data_Crystal16)."}]}